Urethane rheology modifiers substantially free of terminal hydrophobic groups and compositions containing same

ABSTRACT

Rheology modifiers useful in water-based and organic solvent-based compositions are derived from the reaction of polyalkylene oxide, polyfunctional material, diisocyanate and little or no water. The modifiers are characterized by having a branched structure and containing substantially no terminal hydrophobic groups.

BACKGROUND OF THE INVENTION

This invention relates to rheology modifiers. More particularly, the invention relates to urethane rheology modifiers especially useful in water and organic solvent-based compositions.

Additives have long been used in coating compositions for various purposes. Thus, viscosity control agents, surfactants, sag-control agents, anti-foaming agents and other materials are added to coating compositions in minor amounts for their respective functions. Rheology modifiers are also added to such compositions not only for increasing the viscosity of the coating composition but to maintain the viscosity at desired levels under varying process conditions and end-use situations. Secondary effects obtained from the rheology modifiers include protective colloidal action, improvement in pigment suspension, leveling and flow. Some of these properties are also desired in similar type compositions, for instance textile treating compositions, cosmetics, paper compositions, well drilling, fire-fighting foams, detergents, pharmaceuticals, agricultural formulations, and emulsions of all kinds. It can be seen rheology modifiers are used in a variety of compositions.

Many well-known rheology modifiers are used with varying degrees of success. Thus, natural products such as the alginates, casein, and gum tragacanth and modified natural products such as methyl cellulose and hydroxyethyl cellulose are useful rheology modifiers. Synthetic rheology modifiers have also been used. These materials include the carboxyvinyl ether copolymers, acrylic polymers and maleic anhydride/styrene copolymers. However, the known rheology modifiers have various deficiencies. For example, the natural rheology modifiers are susceptible to biological attack. Synthetic rheology modifiers are not subject to such attack yet most of them do suffer from having less than desirable thickening qualities over a wide range of end uses and/or film forming concentrations.

There is accordingly a need for rheology modifiers which are biologically resistant and which function over a wide range of uses and temperatures. Ideally, such rheology modifiers can be used in water-based as well as organic solvent based systems and can be used with many different film forming resins. An added benefit would be if the rheology modifiers imparted many of the secondary properties described above.

As used herein, all percents and ratios are by weight unless otherwise stated.

SUMMARY OF THE INVENTION

Disclosed herein are rheology modifiers derived from the reaction of 8 moles of a polyalkylene oxide, from about 0.1 to about 3 moles of a polyfunctional material, from about 4 to about 15 moles of a diisocyanate, less than about 3 moles water and additional diisocyanate to compensate for any water present. The rheology modifiers are substantially free of terminal hydrophobic groups and have a branched structure.

The aforedescribed rheology modifiers are useful in water-based as well as organic solvent-based compositions. The rheology modifiers are especially useful in coating compositions.

DETAILED DESCRIPTION OF THE INVENTION

The following paragraphs describe the rheology modifiers, their method of making and various applications thereof. While the discussion of the reaction products which follows is in reference to them as "rheology modifiers," it should be uderstood this term is used broadly. That is, "rheology modifiers" is meant to encompass such terms as thickening agents, thixotropic agents, viscosity modifiers and gelling agents.

The rheology modifiers useful herein are derived from the reaction of polyalkylene oxides, polyfunctional materials, diisocyanates and water. The modifiers have a branched chain structure and are further characterized by having substantially no terminal hydrophobic groups.

Polyalkylene oxides used in the reaction include the polyethylene oxide diols, polypropylene oxide diols and polybutylene oxide diols. These materials have a molecular weight of from about 2,000 to about 20,000, preferably from about 4000 to about 12,000. The aforementioned molecular weights are weight average molecular weights determined by gel permeation chromatography, using a polystyrene standard. The polyethylene oxide is a preferred polyalkylene oxide, especially when the resultant rheology modifier is used in water-based compositions. The reaction mixture consists essentially of 8 moles of the polyalkylene oxide with the remaining reactants' amounts based thereon.

The polyfunctional material has either at least 3 active hydrogens and is capable of reacting with an isocyanate or is a polyisocyanate with at least 3 isocyanate groups. Classes of materials useful as the polyfunctional material include polyols, amines, amine alcohols, thiols and polyisocyanates. The preferred polyfunctional material is a polyol having a hydroxyl functionality of at least three. Examples of such materials include the polyalkylols, e.g., trimethylolpropane, trimethylolethane and pentaerythritol; the polyhydroxyalkanes, e.g., glycerol, erythritol, sorbitol, and mannitol; polyhydric alcohol ethers such as those derived from the aforementioned alcohols and alkylene oxides; cycloaliphatic polyhydric compounds, e.g., trihydroxyl cyclohexanes; and aromatic compounds such as trihydroxybenzene. Preferred polyols are the trifunctional alcohols, especially trimethylolpropane. Additional examples of polyfunctional materials include diethylenetriamine; triethylenetetramine; diethanolamine; triethanolamine; triisopropanolamine; trimercaptomethylpropane; triphenyl methane-4,4',4"-trisocyanate; 1,3,5-triisocyanato benzene; 2,4,6-triisocyanate toluene; 4,4'-diphenyl-dimethyl methane-2,2'-5,5'-tetraisocyanate; and hexamethylene diisocyanate trimer, such as Mobay Chem. Co's Desmodur N. The level of polyfunctional material ranges from about 0.1 moles to about 3 moles, preferably from about 1 mole to about 3 moles of the reaction mixture.

A third component used in the reaction mixture is a diisocyanate at a level of from about 4 moles to about 15 moles, preferably from about 6 moles to about 12 moles. Diisocyanate in addition to these amounts is used if there is water present in the reaction mixture. (As discussed later, water can be present in minor amounts.) As is well known, water consumes isocyanate functionality. Accordingly, an amount of additional diisocyanate based on any water present is also used in the reaction to maintain the stoichiometry of the reaction. Several different hydrocarbon or substituted hydrocarbon diisocyanates are useful including the aliphatic, cycloaliphatic and aromatic diisocyanates either alone or in admixture. Generally available diisocyanates have the formula OCNRNCO where R is arylene, e.g., phenylene and diphenylene; alkylarylene, e.g., dimethylbiphenylene, methylenebisphenyl and dimethylmethylenebisphenylene; alkylene, e.g., methylene, ethylene, tetramethylene, hexamethylene, a 36 methylene species, and trimethylhexylene; and alicyclic, e.g., isophorone and methylcyclohexylene. Still other useful diisocyanates include those of the above formula where R is a hydrocarbon group containing ester or ether linkages. Specific examples of suitable diisocyanates include 1,4-tetramethylene diisocyanate; 1,6-hexamethylene diisocyanate; 2,2,4-trimethyl-1,6-diisocyanato hexane; 1,10-decamethylene diisocyanate; 1,4-cyclohexylene diisocyanate; 4,4'-methylene bis (isocyanato cyclohexane); p-phenylene diisocyanate; 2,6-toluene diisocyanate; 2,4-toluene diisocyanate; xylene diisocyanate; isophorone diisocyanate; bis para-isocyanato cyclohexylmethane; 4,4-biphenylene diisocyanate; 4,4-methylene diphenyl isocyanate; 1,5-naphthalene diisocyanate; and 1,5-tetrahydronaphthalene diisocyanate. Preferred are the toluene diisocyanates and the cycloaliphatic diisocyanates, especially isophorone diisocyanate and bis para-isocyanato cyclohexylmethane.

A fourth component which can be found in the reaction mixture is water. The water is present at a level of less than about 3 moles. Preferably, less than about 2.8 moles of water is used. It should be understood that oftentimes the components other than the diisocyanate used in the reaction as well as any solvent medium used will contain water, usually in trace amounts. It is necessary the water brought into the reaction mixture by these sources be accounted for and adjusted by at least partially drying the reaction mixture. The level of water is found to have an effect on the viscosity modifying characteristics of the rheology modifiers. It is theorized the water is responsible for the formation of urea and other groups within the molecule. While levels of water greater than about 3 moles produce very satisfactory rheology modifiers as disclosed in our commonly assigned copending application, "Rheology Modifiers and Compositions Containing Same," Ser. No. 174,479, filed Aug. 1, 1980, now U.S. Pat. No. 4,298,511 the rheology modifiers of this invention are also useful and are less expensive to make.

Components in addition to those discussed above can be included in the reaction mixture provided they do not interfere with the reaction or materially affect the properties of the resultant rheology modifier. Thus, components such as monofunctional materials, non-polyalkylene oxide polyols and lower molecular weight polyols can be included in the reaction mixture at low levels, generally less than about 10% by weight. Preferably, however, the rheology modifiers of this invention are derived solely from the four components discussed in the paragraphs immediately above.

A convenient method of making the rheology modifier is by blending all the components together in the presence of a solvent medium and heating to a temperature ranging from about 100° C. to about 130° C. Alternatively, the components can be individually added in any order and reacted at the aforementioned elevated temperature. The reaction is allowed to proceed until substantially no free isocyanate groups are present. The absence of free isocyanate groups signals the end of the reaction. The aforementioned reactant ratios assure there will be no free isocyanate groups in the reaction mixture provided the reaction is allowed to proceed to completion. Any of several inert solvents can be used as the solvent medium, the only criteria being that all the components be either soluble or dispersible therein. Thus, benzene, toluene, xylene, ethyl acetate, butyl acetate and the dialkyl ethers of ethylene glycol and diethlyene glycol can be used. Preferred, however, for use as the solvent medium is an organic solvent which is compatible with a water-based or organic solvent-based coating composition. Compatible solvents are preferred since it is a desired objective that the rheology modifier as made be added directly to a coating composition without a need to remove any incompatible solvent medium used in its preparation. This objective is particularly difficult to meet with water-based coating compositions. Solvents found to be especially compatible with the coating compositions, including the water-based compositions, include 1-methyl-2-pyrrolidinone, dimethylformamide, dimethyl acetamide, dimethyl sulfoxide, gamma butyrolactone, dioxane, dimethyl and diethyl ethers of ethylene glycol and diethylene glycol, and acetonitrile.

In a preferred method of making the rheology modifiers, a polyhydric material such as ethylene glycol, propylene glycol, or glycerine is added when the mixture described in the preceding paragraph is substantially free of isocyanate groups. This addition reduces the mixture's viscosity thereby making it easier to handle and further ensures there are no terminal hydrophobic groups in the rheology modifier. For maximum ease of handling, the mixture's temperature is about 100° C. to about 130° C. when the polyhydric material is added. The amount of polyhydric material added can vary widely, generally with amounts from about 50% to about 500% of the polyhydric material, based on the reactive components being used.

The aforedescribed modifiers can be used in water-based compositions as well as organic solvent-based compositions. They are most useful in coating compositions, as below described, especially the water-based latex coating compositions.

Latex coating compositions can be made from many different water-insoluble polymeric film-forming materials which are capable of forming a dispersion in water. Especially useful film-forming polymeric resins are the acrylic resins which are the polymerized ester derivatives of acrylic acid and methacrylic acid. The esters are formed by the reaction of acrylic or methacrylic acid with a suitable alcohol, e.g., methyl alcohol, ethyl alcohol, propyl alcohol and butyl alcohol. Generally speaking, the larger the alcoholic portion of the ester, the softer or more flexible the resultant resin. Monomers such as styrene, vinyl toluene, vinyl chloride and vinylidene chloride can be reacted with the acrylic and methacrylic esters to produce resins having excellent properties. Copolymers of acrylic resins with each other or with other monomers of acrylic or methacrylic acids and their derivatives such as methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, acrylamide, and acrylonitrile are useful. Still other polymeric resins include the vinyl resins derived from monomers containing a carbon to carbon double bond. These monomers polymerize by linear addition to form long-chain molecules. The vinyl monomers can have various pendant groups such as chlorine, acetate and aromatic groups. The vinyl resins are commonly derived from monomers such as vinyl chloride, vinylidene chloride, vinyl acetate, styrene, acrylonitrile and mixtures thereof.

The water-insoluble polymeric resins have a particle diameter of less than about 1 micron, preferably from about 0.05 microns to about 0.5 microns and are suspended in water. These compositions are oftentimes referred to as either emulsions or latexes. A typical latex coating composition contains from about 5% to about 70%, preferably from about 20% to aboug 35% of the aforedescribed film-forming polymeric resins and from about 0.1% to about 10%, preferably from about 1% to about 5%, based on the film-forming of polymeric resin, if the rheology modifier.

Other film-forming resins which can be either water-solubilized or dissolved in organic solvents include the epoxy, vinyl, alkyd, polyester, acrylic, aminoplast, phenoplast, cellulose derivatives, amide or urethane resins or mixtures thereof. Copolymers derived from such resins are also useful. These resins are further described in commonly assigned U.S. Ser. No. 166,643, filed July 7, 1980, Becher et al, "Pigment Dispersants for Coating Compositions", the disclosure of which is herein incorporated by reference.

Several different organic solvents can be used as a liquid carrier for the coating compositions. Examples of such solvents include hydrocarbons and halogenated hydrocarbons such as toluene, xylene, mineral spirits, hexane, cyclohexane, chlorobenzene and perchloroethylene.

Additives commonly used in coating compositions can be used. Such additives include plasticizers, fillers, surfactants, stabilizers and pigments.

The coating compositions are applied by conventional coating techniques onto a variety of substrates. Thus the compositions can be applied by spraying, dipping, brushing, flowcoating and rollcoating. Substrates that can be coated include wood, metals, glass, plastics, and wallboard.

The examples which follow are illustrative of the invention.

EXAMPLE I

A rheology modifier is derived from the following reactants according to the procedure set out below:

    ______________________________________                                                         Molar ratio                                                    ______________________________________                                         Polyethylene oxide                                                                               8                                                            (M.W. 8000)                                                                    Trimethylolpropane                                                                               1.4                                                          Dimer diisocyanate (1)                                                                           11.7                                                         Water             2.5                                                          ______________________________________                                          (1) Available from Henkel Corp. as DDI.                                  

A reaction vessel is initially charged with 400 parts 1-methyl-2-pyrrolidinone (available from GAF Corp. and hereinafter referred to as M-pyrol), 100 parts cyclohexane, 500 parts polyethylene oxide (available from Union Carbide Corp. as Carbowax 6000) and 1.5 parts trimethylolpropane. The reaction vessel is now heated to about 105° C. to remove water and then to 150° C. to remove cyclohexane. A total of 66.4 parts water and cyclohexane is removed. A sample of the mixture shows there to be 0.037% water present. A 1% dibutyl tin dilaurate catalyst solution in M-pyrol is then added at a level of 10 parts while maintaining the reaction temperature at 100° C. Fifty three and nine tenths (53.9) of dimer diisocyanate is next added using an isocyanate pump, followed by a rinse with 10 parts M-pyrol. After about a three-hour hold period, an addition of 1548 parts propylene glycol is made. The viscosity of the mixture is determined to be Z-6. After another hold period of about 3 and 1/2 hours at 120° C., 502 parts propylene glycol and 502 parts deionized water are added. The final reaction mixture has a viscosity of Z-3 and a 15% solids content.

EXAMPLE II

The rheology modifier of this example contains the following reactants:

    ______________________________________                                                            Molar ratio                                                 ______________________________________                                         Polyethylene oxide (M.W. 8000)                                                                      8                                                         Trimethylolpropane   1.4                                                       Diisocyanate (1)     11.9                                                      Water                2.3                                                       ______________________________________                                          (1) The diisocyanate is derived from the reaction of 2 moles toluene           diisocyanate and 1 mole of a neopentyl glycol adipate. The neopentyl           glycol adipate is made by reacting 2 moles of neopentyl glycol and 1 mole      adipic acid until an acid number of less than 5 is obtained.             

A reaction vessel set up as in Example I is charged with 500 parts of the polyethylene oxide, 1.5 parts trimethylolpropane, 335 parts M-pyrol and 100 parts cyclohexane. This mixture is heated to 150° C. to strip off 66.4 parts water and cyclohexane. A sample of the mixtures shows there to be 0.037% water present. Ten (10) parts of a 1% dibutyl tin dilaurate solution in M-pyrol is added while the mixture is maintained at 100° C. At this point, 213.2 parts of the diisocyanate and 26 parts M-pyrol rinse are added. The reaction mixture is isocyanate-free after about 41/2 hours. The viscosity of the mixture is reduced by adding 2539 parts propylene glycol and 621 parts water.

EXAMPLE III

The rheology modifiers of Examples I and II are tested using the following latex coating composition.

    ______________________________________                                                              Parts by Weight                                           ______________________________________                                         Acrylic latex (1)      368                                                     Rheology modifier solution (15% solids)                                                               50                                                      Water                  148                                                     Amino methyl propanol  1                                                       Dispersant (2)         2                                                       Surfactant (3)         12                                                      Defoamer (4)           8                                                       Phenyl mercuric acetate                                                                               0.5                                                     Calcium carbonate      119                                                     Barium sulfate         190                                                     Hydroxyethyl cellulose 2                                                       Coalescent (5)         12                                                      Ethylene glycol        15                                                      Clay slurry (68% solids)                                                                              104                                                     ______________________________________                                          (1) Available from Rohm & Haas Co. as AC490, 46.5% solids.                     (2) Available from Rohm & Haas Co. as Tamol 731.                               (3) A blend of Strodex SEB30 (Dexter Chem. Co.), Igepal COQ10 (General         Amiline & Film Corp.) and Triton GR7M (Rohm & Haas Co.), in a 2:8:2            ratio.)                                                                        (4) Available from Drew Chem. Co. as DREW L475.                                (5) Available from the Dow Chem. Co. as Dalpad A.                        

Viscosities of the above coating composition where the rheology modifiers are separately used are as follows:

    ______________________________________                                                    Viscosity of Composition (centipoises)                              Rheology modifier                                                                           6 rpm         60 rpm                                              ______________________________________                                         Example I     3,200        5,550                                               Example II   32,500        7,700                                               ______________________________________                                    

EXAMPLE IV

An organic solvent based composition containing a rheology modifier is formulated as follows:

    ______________________________________                                                             Parts by Weight                                            ______________________________________                                         Long oil/soya alkyd resin                                                                            17.33                                                    Sunflower/soya alkyd resin                                                                           31.09                                                    Rheology modifier solution of Example I                                        (15% solids)          1.67                                                     Mineral spirits       13.14                                                    Ethylene glycol monophenyl ether                                                                     1.63                                                     Soya lecithin         0.42                                                     Cobalt feeder drier   0.05                                                     Calcium drier         0.39                                                     Cobalt drier          0.06                                                     Manganese drier       0.03                                                     Zirconium drier       0.62                                                     Surfactant (1)        0.47                                                     Surfactant (2)        0.24                                                     Aluminum silicate     2.33                                                     Silica                2.27                                                     Calcium carbonate     15.51                                                    Titanium dioxide      8.33                                                     Soya oil              3.25                                                     Methyl ethyl ketoxime 0.46                                                     ______________________________________                                          (1) Available from General Aniline and Film Co. as Igepal CO 430.              (2) Available from Atlas Chem. Industries as Atlas G3300.                

After 24 hours, the above compostion has a viscosity of 89 Kreb units versus 76 Kreb units for the same composition without the rheology modifier, thereby demonstrating the utility of the rheology modifiers of this invention in organic solvent-based compositions.

The above examples illustrate the rheology modifiers of the invention and their use in latex and organic solvent based coating compositions. 

What is claimed is:
 1. A urethane rheology modifier characterized in having a branched structure, substantially no terminal hydrophobic groups and capable of modifying the rheology properties of water-based and organic solvent-based compositions, derived from the reaction of (a) for each 8 moles of a polyalkylene oxide having a molecular weight of from about 2,000 to about 20,000; (b) from about 0.1 mole to about 3 moles of a polyfunctional material, said material having at least 3 active hydrogens capable of reacting with isocyanate or being a polyisocyanate having at least three isocyanate groups; (c) from about 4 moles to about 15 moles of a diisocyanate; (d) less than about 3 moles water; and (e) an amount of additional diisocyanate to compensate for any water which is present and capable of consuming isocyanate functionality.
 2. The rheology modifier of claim 1 wherein the polyfunctional material is selected from the group consisting of polyols, amines, amine alcohols, thiols, polyisocyanates, and mixtures thereof.
 3. The rheology modifier of claim 2 wherein the polyfunctional material is the polyisocyanate.
 4. The rheology modifier of claim 2 wherein the polyfunctional material is the polyol.
 5. The rheology modifier of claim 4 wherein the polyol is a trifunctional alcohol.
 6. The rheology modifier of claim 5 wherein the trifunctional alcohol is trimethylolpropane.
 7. The rheology modifier of claim 1 or 6 wherein the polyalkylene oxide is a polyethylene oxide.
 8. The rheology modifier of claim 7 wherein the polyethylne oxide has a molecular weight of from about 4000 to about 12,000.
 9. The rheology modifier of claim 8 wherein the diisocyanate is selected from the group consisting of toluene diisocyanate, isophorone diisocyanate, bis para-isocyanato cyclohexylmethane and mixtures thereof.
 10. The rheology modifier of claim 1 wherein the rheology modifier is derived from the reaction of (a) for each 8 moles of the polyalkylene oxide; (b) from about 1 mole to about 3 moles of the polyfunctional material; (c) from about 6 moles to about 12 moles of the diisocyanate; (d) less than about 2.8 moles water; and (e) an amount of additional diisocyanate to compensate for any water present.
 11. The rheology modifier of claim 10 wherein polyethylene oxide, trimethylolpropane, bis para-isocyanato cyclohexylmethane and water are reacted.
 12. A process for making a urethane rheology modifier characterized in having a branched structure, substantially no terminal hydrophobic groups and capable of modifying the rheology properties of water-based and organic solvent-based compositions, comprising(1) blending in an inert organic solvent (a) for each 8 moles of a polyalkylene oxide having a molecular weight of from about 2,000 to about 20,000, (b) from about 0.1 mole to about 3 moles of a polyfunctional material, said material having at least 3 active hydrogens capable of reacting with isocyanate or being a polyisocyanate having at least 3 isocyanate groups, (c) from about 4 moles to about 15 moles of a diisocyanate, (d) less than about 3 moles water, and (e) an amount of additional diisocyanate to compensate for any water which is present and capable of consuming isocyanate functionality; and (2) reacting the mixture of step (1) until substantially no free isocyanate groups are present, so as to form the rheology modifier.
 13. The process of claim 12 wherein the organic solvent is compatible with a water-based coating composition.
 14. The process of claim 12 wherein the organic solvent is compatible with an organic solvent-based coating composition.
 15. The process of claim 13 wherein the organic solvent is selected from the group consisting of 1-methyl-2-pyrrolidinone, dimethylformamide, dimethyl acetamide, gamma butyrolactone, dioxane, acetonitrile, dimethyl and diethyl ethers of ethylene glycol and diethylene glycol, and mixtures thereof.
 16. The process of claim 15 wherein the organic solvent is 1-methyl-2-pyrrolidinone.
 17. The process of claim 13 wherein a polyhydric material is added after substantially no free isocyanate groups are present.
 18. The process of claim 17 wherein the polyhydric material is selected from the group consisting of ethylene glycol, propylene glycol, glycerine, and mixtures thereof.
 19. The process of claim 18 wherein the polyhydric material is propylene glycol.
 20. The process of claim 17 wherein the temperature of the mixture is maintained at from about 100° C. to about 130° C. while the polyhydric material is added.
 21. The process of claim 12 wherein the mixture of step (1) is reacted at a temperature ranging from about 100° C. to about 130° C.
 22. The process of claim 12 wherein the polyfunctional material is selected from the group consisting of polyols, amines, amine alcohols, thiols, polyisocyanates and mixtures thereof.
 23. The process of claim 22 wherein the polyfunctional material is the polyisocyanate.
 24. The process of claim 22 wherein the polyfunctional material is a trifunctional alcohol.
 25. The process of claim 24 wherein the polyalkylene oxide is a polyethylene oxide having a molecular weight of from about 4,000 to about 12,000.
 26. The process of claim 25 wherein the diisocyanate is selected from the group consisting of toluene diisocyanate, isophorone diisocyanate, bis para-isocyanato cyclohexylmethane and mixtures thereof.
 27. The process of claim 26 wherein the mixture of step (1) comprises (a) for each 8 moles of the polyalkylene oxide, (b) from about 1 mole to about 3 moles of the polyfunctional material, (c) from about 6 moles to about 12 moles of the diisocyanate; (d) less than about 2.8 moles water; and (e) an amount of additional diisocyanate to compensate for any water present.
 28. The process of claim 27 wherein polyethylene oxide, trimethylolpropane, bis para-isocyanato cyclohexylmethane and water are reacted.
 29. A coating composition consisting essentially of a film forming polymeric resin and about 0.1% to about 10%, based on the film forming polymeric resin solids, of a rheology modifier, said modifier characterized in having a branched structure, substantially no terminal hydrophobic groups and derived from the reaction of (a) for each 8 moles of a polyalkylene oxide having a molecular weight of from about 2,000 to about 20,000, (b) from about 0.1 mole to about 3 moles of a polyfunctional material, said material having at least 3 active hydrogens capable of reacting with isocyanates or being a polyisocyanate having at least 3 isocyanate groups; (c) from about 4 moles to about 15 moles of a diisocyanate; (d) less than about 3 moles water; and (e) an amount of diisocyanate to compensate for any water which is present and capable of consuming isocyanate functionality.
 30. The composition of claim 29 wherein the polyfunctional material is selected from the group consisting of polyols, amines, amine alcohols, thiols, polyisocyanates, and mixtures thereof.
 31. The composition of claim 30 wherein the polyfunctional material is the polyisocyanate.
 32. The composition of claim 30 wherein the polyfunctional material is the polyol.
 33. The composition of claim 32 wherein the polyol is a trifunctional alcohol.
 34. The composition of claim 33 wherein the trifunctional alcohol is trimethylolpropane.
 35. The composition of claim 31 or 32 wherein the polyalkylene oxide is polyethylene oxide having a molecular weight of from about 4000 to about 12,000.
 36. The composition of claim 35 wherein the diisocyanate is selected from the group consisting of toluene diisocyanate, isophorone diisocyanate, bis para-isocyanato cyclohexylmethane and mixtures thereof.
 37. The composition of claim 29 wherein the rheology modifier is derived from (a) for each 8 moles of the polyalkylene oxide; (b) about 1 mole to about 3 moles of the polyfunctional material; (c) about 6 moles to about 12 moles of the diisocyanate; (d) less than about 2.8 moles water; and (e) an amount of additional diisocyanate to compensate for any water present.
 38. The composition of claim 29 wherein the film-forming resin is an epoxy, vinyl, alkyd, polyester, acrylic, aminoplast, phenolplast, cellulose derivative, amide or urethane resin or mixture thereof.
 39. The composition of claim 29 wherein the film-forming resin is a latex resin.
 40. The composition of claim 39 wherein the composition contains from about 5% to about 70% of the polymeric film-forming resin. 